Material D2 Tool Steel Round Bar 1-3/4 ASTM A681 2008 Die Steel Rod

Product Categories

Bright Round Bar [20]
Cold Drawn Round Bar [19]
Spring Steel Round Bar [16]
Alloy Structural Steel [21]
Low Alloy Steel Bar [12]
Bright Steel Round Bar [16]
Free Cutting Steel Bar [17]
Carbon Steel Bright Bar [19]
Stainless Steel Bright Round Bar [19]
Die Steel Bar [8]
Structural Steel Shapes [7]
Gear Bright Round Steel [6]

Wuxi Zhanlu International Trade Co., Ltd

Trust Seal

Verified Supplier

Credit Check

Supplier Assessment

Contact Now

Material D2 Tool Steel Round Bar 1-3/4 ASTM A681 2008 Die Steel Rod

Name: Material D2 Tool Steel Round Bar 134 ASTM A681 2008 Die Steel Rod
Brand: Zhanlu
Price: 1 USD

Brand Name : Zhanlu

Model Number : D2

Place of Origin : China

MOQ : Consultation

Price : Consultation

Payment Terms : L/C, T/T

Supply Ability : Consulting service

Delivery Time : 5-8Workdays

Packaging Details : Conventional packaging

Name : D2 Die steel

Material : D2

Diameter : 6.0mm-500mm

Length : 2.5m-10m

Type : ASTM A681 - 2008 round bar

Application : Suitable for tool steel with complex deformation, various kinds of cold stamping dies with high wear resistance and long service life, cold cutting blades, and thread rolling plates; Cold extrusion forming, drawing film, stainless steel sheet and balance c

Contact Now

D2 Die steel ASTM A681 - 2008 Hot rolled / bright round bar

D2 steel has high wear resistance, micro-deformation cold working die steel, and wind-hardened tool steel, with carbon content up to 1.5%, chromium content up to 11.5%, and hardness up to 60HRC after heat treatment. D2 steel, such as silicon steel sheet punching die, cold cutting scissors, trimming die, etc. High wear resistance, vacuum heat treatment to HRC60 ° - 62 °, excellent processing performance.

Supply Form & Size

Form of Supply	Size(mm)	Length(mm)
Round bar	6.0mm-500mm	2.5m-10m

Chemical Composition&Related Specifications

Grade	C	Mn	Cr	Mo	V	Co	P	S	Si
D2	1.4-1.6	≤0.6	11.0-13.0	0.70-1.20	≤1.1	≤1.0	≤0.30	≤0.30	≤0.60

Brand comparison table

AISI/SAE	DIN/EN	BS	JIS/KS	China
D2	X153CrMoV12	X153CrMoV12	SKD11	Cr12Mo1V1

Mechanical Property

Heat treatment specification	Quenching, 820 ± 15 ℃ preheating, 1000 ± 6 ℃ (salt bath) or 1010 ± 6 ℃ (furnace controlled atmosphere) heating, heat preservation for 10-20 min, air cooling, 200 ± 6 ℃ tempering
Quenching:	Slowly raise the temperature of the workpiece to 600 ℃, hold it for 20 min for the first preheating, and then rise to 850 ℃ after the average temperature, and hold it for 30 min for the second preheating, and finally raise the temperature to 1020~1040 ℃, hold it for 25~40 min, and then discharge it for air cooling.
Stress relief annealin	After rough machining, the workpiece shall be heated to 600~650 ℃, kept for 2h, cooled to 500 ℃ with the furnace, and then discharged for air cooling

Material D2 Tool Steel Round Bar 1-3/4 ASTM A681 2008 Die Steel Rod

Product Tags: